SAMPLE HIGH DENSITY POLYETHYLENE (HDPE) GEOMEMBRANE LINER PHYSICAL DATA SPECIFICATIONS
|
.040" (40MIL) SMOOTH
HDPE SPECIFICATION
|
| PROPERTY |
TEST METHOD |
FREQUENCY (FT2) |
PROPERTY VALUE |
| Thickness (mils) |
ASTM D-5199 |
Every Roll |
Average 40 |
|
|
|
|
Minimum 36 |
|
| Tensile (ppi) |
ASTM D-638 |
25,000 |
MIN. |
TYP. |
| Strength at Yield
(ppi) |
|
|
84 |
95 |
| Elongation at Yield |
|
|
12% |
13% |
| Strength at Break |
|
|
152 |
160 |
| Elongation at Break |
(2.5" gage
length) |
|
560% |
600% |
| Tear Resistance (lbs) |
ASTM D-1004 |
50,000 |
26 |
30 |
| Puncture Resistance |
FTMS 101C/2065 |
50,000 |
48 |
52 |
| Density (g/cc) |
ASTM D-792 |
100,000 |
0.94 |
|
| Carbon Black Content
(%) |
ASTM D-1603 |
100,000 |
2.0-3.0 |
|
| Carbon Black
Dispersion |
ASTM D-3015 |
100,000 |
A1,A2,B1 |
|
| Melt Index (g/10min) |
ASTM D-1238 |
Resin Batch |
<0.5 |
|
| Dimensional Stability
(% change max) |
ASTM D-1204 |
Resin Batch |
±2 |
|
| Environmental Stress
Crack (HR) |
ASTM D-1693 |
Certified |
1,500 |
|
| Low Temperature
Brittleness |
ASTM D-746 |
Certified |
-60°C |
|
| Bonded Seam Strength
(ppi) |
ASTM D-4437 |
Shear |
80 |
|
|
|
Peel (Fusion) |
57 |
|
|
|
Peel (Extrusion) |
52 |
|
|
.060" (60MIL) SMOOTH
HDPE SPECIFICATION
|
| PROPERTY |
TEST
METHOD |
FREQUENCY
(FT2) |
PROPERTY VALUE |
| Thickness (mils) |
ASTM D-5199 |
Every Roll |
Average 60 |
|
|
|
|
Minimum 54 |
|
| Tensile (ppi) |
ASTM D-638 |
25,000 |
MIN. |
TYP. |
| Strength at Yield
(ppi) |
|
|
126 |
140 |
| Elongation at Yield |
|
|
12% |
13% |
| Strength at Break |
|
|
228 |
240 |
| Elongation at Break |
(2.5" gage
length) |
|
560% |
600% |
| Tear Resistance (lbs) |
ASTM D-1004 |
50,000 |
39 |
45 |
| Puncture Resistance |
FTMS 101C/2065 |
50,000 |
72 |
80 |
| Density (g/cc) |
ASTM D-792 |
100,000 |
0.94 |
|
| Carbon Black Content
(%) |
ASTM D-1603 |
100,000 |
2.0-3.0 |
|
| Carbon Black
Dispersion |
ASTM D-3015 |
100,000 |
A1,A2,B1 |
|
| Melt Index (g/10min) |
ASTM D-1238 |
Resin Batch |
<0.5 |
|
| Dimensional Stability
(% change max) |
ASTM D-1204 |
Resin Batch |
±2 |
|
| Environmental Stress
Crack (HR) |
ASTM D-1693 |
Certified |
1,500 |
|
| Low Temperature
Brittleness |
ASTM D-746 |
Certified |
-60°C |
|
| Bonded Seam Strength
(ppi) |
ASTM D-4437 |
Shear |
120 |
|
|
|
Peel (Fusion) |
84 |
|
|
|
Peel (Extrusion) |
78 |
|
|
.080" (80MIL) SMOOTH
HDPE SPECIFICATION
|
| PROPERTY |
TEST
METHOD |
FREQUENCY
(FT2) |
PROPERTY VALUE |
| Thickness (mils) |
ASTM D-5199 |
Every Roll |
AVERAGE 80 |
|
|
|
|
MINIMUM 72 |
|
| Tensile (ppi) |
ASTM D-638 |
25,000 |
MIN. |
TYP. |
| Strength at Yield
(ppi) |
|
|
168 |
190 |
| Elongation at Yield |
|
|
12% |
13% |
| Strength at Break |
|
|
304 |
320 |
| Elongation at Break |
(2.5" gage
length) |
|
560% |
600% |
| Tear Resistance (lbs) |
ASTM D-1004 |
50,000 |
52 |
55 |
| Puncture Resistance |
FTMS 101C/2065 |
50,000 |
96 |
105 |
| Density (g/cc) |
ASTM D-792 |
100,000 |
0.94 |
|
| Carbon Black Content
(%) |
ASTM D-1603 |
100,000 |
2.0-3.0 |
|
| Carbon Black
Dispersion |
ASTM D-3015 |
100,000 |
A1,A2,B1 |
|
| Melt Index (g/10min) |
ASTM D-1238 |
Resin Batch |
<0.5 |
|
| Dimensional Stability
(% change max) |
ASTM D-1204 |
Resin Batch |
±2 |
|
| Environmental Stress
Crack (HR) |
ASTM D-1693 |
Certified |
1,500 |
|
| Low Temperature
Brittleness |
ASTM D-746 |
Certified |
-60°C |
|
| Bonded Seam Strength
(ppi) |
ASTM D-4437 |
Shear |
160 |
|
|
|
Peel (Fusion) |
114 |
|
|
|
Peel (Extrusion) |
104 |
|
|
.100" (100MIL) SMOOTH
HDPE SPECIFICATION
|
| PROPERTY |
TEST
METHOD |
FREQUENCY
(FT2) |
PROPERTY VALUE |
| Thickness (mils) |
ASTM D-5199 |
Every Roll |
AVERAGE
100 |
|
|
|
MINIMUM 90 |
|
| Tensile (ppi) |
ASTM D-638 |
25,000 |
MIN. |
TYP. |
| Strength at Yield
(ppi) |
|
|
210 |
240 |
| Elongation at Yield |
|
|
12% |
13% |
| Strength at Break |
|
|
380 |
400 |
| Elongation at Break |
(2.5" gage
length) |
|
560% |
600% |
| Tear Resistance (lbs) |
ASTM D-1004 |
50,000 |
65 |
72 |
| Puncture Resistance |
FTMS 101C/2065 |
50,000 |
120 |
130 |
| Density (g/cc) |
ASTM D-792 |
100,000 |
0.94 |
|
| Carbon Black Content
(%) |
ASTM D-1603 |
100,000 |
2.0-3.0 |
|
| Carbon Black
Dispersion |
ASTM D-3015 |
100,000 |
A1,A2,B1 |
|
| Melt Index (g/10min) |
ASTM D-1238 |
Resin Batch |
<0.5 |
|
| Dimensional Stability
(% change max) |
ASTM D-1204 |
Resin Batch |
±2 |
|
| Environmental Stress
Crack (HR) |
ASTM D-1693 |
Certified |
1,500 |
|
| Low Temperature
Brittleness |
ASTM D-746 |
Certified |
-60°C |
|
| Bonded Seam Strength
(ppi) |
ASTM D-4437 |
Shear |
200 |
|
|
|
Peel (Fusion) |
130 |
|
|
|
Peel (Extrusion) |
120 |
|
|
|